DESCRIPTION
|
|
Cement based bonding
mortar with low mixture density and with polymer additives.
|
 |
|
APPLICATION
FIELDS |
For constructing
brick walls and bims walls.
|
|
PREPARATION OF
SURFACE |
1. The application
surface must be free of all dust, dirt, paint, grease etc.
2. The application surface must be humidified with water.
|
|
APPLICATION |
1. 25 kg. of BETOX
Brick-Bims Bonding Mortar is prepared by adding 5 to 6 lt. of
water with a low speed mixer, until it reaches a paste- like
appearence.
2. The Betox Brick-Bims Bonding Mortar is left to rest for 5
minutes, mixed again to ensure homogeneity and applied on the
prepared
surface using a steel trowel.
3. The application must be made under +5 °C to +35°C.
4. The mixture is applied on to vertical and horizontal surfaces
by trowel.
5. Bricks are is set by mallet and the edges are levelled.
6. The surface must be humidified under windy conditions and
very high temperatures.
|
|
CAUTION |
1. Using gloves is
recommended during use.
2. As the product is cement based, it must not be inhaled, and
rinsed with water in case of contact with skin or eyes.
3. Do not use any other additives when preparing BETOX
Brick-Bims Bonding Mortar.
4. It must be stored under dry conditions stacking 10 vertical
rows at most. |
|
COLOR |
Grey
|
|
|
SHELF LIFE |
One year from the
date of production if kept in a dry place free of humidity. The
cover of a container must be closed tightly when it is not being
used.
TOXICITY: Not toxic. |
|
|
|
|
TECHNICAL FIGURES |
|
Application
Temperature |
+5 C - +
35 C |
|
Apperance ( Color) |
Grey |
|
Water mixing ratio |
5 - 6
Lt. / 25 Kg. |
|
Dry bulk density of hardened mortar
|
1400
± 1600
kg/m3 |
|
Compressive strength of hardened mortar
|
M5 class
(N/mm2) |
Water absorption coefficient due to capillary
action of hardened mortar |
max 1,5
kg/m2 min0,5 |
|
Coefficient
of vapour permeability of hardened mortar |
M value
(15/35) |
|
Coefficient of thermal conductivity
|
max
0,600 W/mK |
|
Workable life time of fresh mortar
|
min 180
minutes |
|
Water-soluble chloride content of fresh mortar
|
max % 0,095 |
|
Initial shear strentgh
|
min 0,3 N/mm2 |
|
Reaction to fire
|
A1 class |
|
Packaging |
25 Kg |
|